Abstract
AbstractThe thermomechanical properties of poly(lactide) (PLA) are strongly related to its semicrystalline microstructure and morphology. Thermal annealing is a strategy to improve the crystallinity of PLA. However, the different techniques and specimen types needed for each kind of characterization could lead to misleading conclusions. In this work, annealed samples of three PLA grades with different molecular weights were studied by DSC, wide angle X‐ray scattering and polarized optical microscopy (POM) and the results are related to their thermomechanical and impact properties. Special focus is put on the POM results obtained by different approaches and the suitability of each of them to be related to the thermomechanical properties. By annealing medium molecular weight PLA specimens at 140 °C an important increase of the heat distortion temperature was obtained, which was not related to the spherulite size but to the combination of high crystallinity degree together with high α/α′ crystal type ratio. However, the impact properties of annealed PLA decreased with increase in the annealing temperature according to an increment in crystallinity and in the α/α′ crystal ratio. © 2019 Society of Chemical Industry
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.