Abstract
Abstract Dry sliding tests were conducted at room temperature and 400 °C on a copper-tungsten composite material paired with martensitic stainless steel disc. The friction coefficient was seen to reduce for room temperature tests at high velocity, whereas it increased for high-temperature tests for the same testing conditions. The pin wear reduced with an increase in velocity and was always mild in nature. High oxide coverage, containing copper and iron were seen on the surface of the friction material as well as counterface. The magnitude of the coverage increased with velocity and temperature. Yates’ statistical method was utilized to analyze parameters that influenced the friction coefficient, pin wear and the (Cu + Fe)/O ratio, in comparison with a reference copper-tin based composite.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.