Abstract
Melt-derived glass ceramics were prepared having the following chemical composition 33SiO2-21CaO-32.5Na2O-12P2O5-1.5MgO (mol %). Samples were sintered at three different temperatures (750, 800, and 850 °C). Thermal, structural, and bioactivity analyses were carried out using TGA-DSC, XRD, and in vitro immersion tests, respectively. XRD results indicated that CaSiO3 was the major phase while Na2Ca2Si3O9 was the minor phase in a glass matrix. The crystallite size and degree of crystallization increased with sintering temperature. Additionally, SEM images showed grain growth and reduction of pores with increasing sintering temperature. The bioactivity of the specimens were assessed by XRD; all specimens exhibited hydroxyapatite phase on their surfaces after immersion in a simulated body fluid, indicating the bioactive nature of the material. Further, the sample sintered at 750 °C was observed to be more bioactive as indicated by crystallization of Ca10(PO4)6(OH)2 on its surface. These results indicate that sintering at high temperature increases the crystallinity, microhardness and chemical stability of this bioactive glass ceramic.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.