Abstract
A multilayer film having overall composition Fe 50Cr 25Ni 25, was irradiated successively by 80 MeV Si ions and Ag ions of 150 and 200 MeV energy. The energy deposited in the multilayer in the form of electronic excitations results in significant modification at the interfaces. The interfacial roughness increases in the system after the irradiations as revealed by X-ray reflectivity measurement. Mössbauer measurements provide evidence of intermixing after the irradiation by 200 MeV Ag ions. Comparison of heavy ion irradiated multilayer has been done with annealed and low energy ion irradiated samples. Results suggest that the phases formed at the interfaces of iron as a result of electronic energy loss are similar to those in the cases of thermal diffusion and keV energy ion beam irradiation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.