Abstract
(CZTSSe) thin films were prepared by sulfurization of evaporated precursor thin films. Precursor was prepared using evaporation method at room temperature. The sulfurization was carried out in a graphite box with S powder at different temperatures. The temperatures were varied in a four step process from to . The effects of the sulfurization temperature on the micro-structural, morphological, and compositional properties of the CZTSSe thin films were investigated using X-ray diffraction (XRD), Raman spectra, field emission scanning electron microscopy (FE-SEM), and transmission electron microscopy (TEM). The XRD and Raman results showed that the sulfurized thin films had a single kesterite crystal CZTSSe. From the FE-SEM and TEM results, the (MoSSe) interfacial layers of the sulfurized CZTS thin films were observed and their thickness was seen to increase with increasing sulfurization temperature. The microstructures of the CZTSSe thin films were strongly related to the sulfurization temperatures. The voids in the CZTSSe thin films increased with the increasing sulfurization temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.