Abstract
Due to the local heating of welding, deformation will occur on the welding structure. To mitigate this deformation, the method called stretching technology was proposed by previous study. In this method, plate was stretched to certain pre-strain, kept in this condition and then welded to another sheet. It can reduce the welding deformation significantly. However, pre-strain will change the properties of joined materials and lead different behavior of welded materials. It will be complicated if dissimilar metals are welded due to different physical and metallurgical properties. Carbon steel SS400 with the thickness of 3.0 mm and 1.0 mm thick-low nickel stainless steel were welded using resistance spot welding (RSW) process with constant electrode pressure and weld time of 6 kN and 5 second respectively. During welding process, low nickel stainless steel was stretched in four different levels pre-strain of 0%, 1%, 1.5% and 2%. Welding current were varied in the range from 3.02 to 4.20 kA. Microstructure investigations and tensile-shear tests were conducted to evaluate the weldability of RSW joint. Generally, stretching during welding process decreased the fussion zone area of RSW joint. In the low welding current, there is no fussion in the interface of stretched plate, but fussion still occured in the interface of unstretched plate. In all levels of welding current, stretching during welding decreased fussion zone area and led to decrease tensile-shear load bearing capacity of RSW joint.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call