Abstract
In order to study the effect of the withdrawing rate on carbide morphology, MC-type carbide in single crystal superalloy AM3 was systematically investigated with sample growth rates from 3.5 μm/s to 500 μm/s. The carbide morphologies were investigated by scanning electron microscopy (SEM), and the electron probe microanalysis (EPMA) was used to characterize the carbide composition. The results indicate that the solidification rate is the important factor governing MC carbide growth morphology, size and distribution, composition and growth mechanism. With the increase of withdrawing rate, nodular, rod-like, Chinese script types of carbide morphology are observed. For the low withdrawing rate, with the increase of withdrawing rate, the carbide size becomes larger. For the case of dendritic interface, the carbide size becomes smaller with refinement of dendrites as withdrawing rate increases. The volume fraction of carbides increases with the withdrawing rate increasing.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.