Abstract
Objective: To evaluate the effect of sandblasting on bending strength and subcritical crack growth (SCG) under cyclic loading of yttria-stabilized tetragonal zirconia polycrystal (Y-TZP) ceramics. Methods: After being polished, sixty bar-shaped specimens of Y-TZP (Wieland zirconia ceramics) were assigned to two groups (n=30) according to the random number table, the sandblasting group (SG) which was treated with sandblasting and the control group (CG) which remained untouched. In each group, half of the specimens (n=15) were subjected to bending strength test, and the results were examined by Weibull statistics and analyzed with ANOVA. The other 15 specimens in each group were subjected to fatigue tests. The results were examined by Weibull statistics and subcritical crack propagation rates were calculated. Results: The bending strengths of SG and CG were (1 291±133) and (1 140±124) MPa (F=10.117, P=0.004), and the Weibull modules of the two groups were 11.06 and 10.64 respectively. The crack growth rate of SCG of SG was lower than that of CG under the same cyclic loading. Conclusions: Proper sandblasting on Y-TZP ceramic can increase its bending strength and resistance to SCG.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Zhonghua kou qiang yi xue za zhi = Zhonghua kouqiang yixue zazhi = Chinese journal of stomatology
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.