By adding various concentrations of rare earth cerium into the acidic hypophosphite plating baths, electroless Ni-P-PTFE coatings have been successfully deposited on the surface of shaft made of mild steel. Surface morphology, microhardness and interfacial adhesion of the coatings were characterized by scanning electron microscope equipped with energy dispersive spectrometer, vicker microhardness meter and WS-92 scrape instrument, respectively. Ring-plate wear test was applied to study the friction coefficient and wear resistance of Ni-P-PTFE coating. Results revealed that Ni-P-PTFE coatings deposited with 10ppm or 20ppm cerium in the plating baths show low friction coefficient and high interfacial adhesion,leading to its perfect wear resistance. However, both the interfacial adhesion and wear resistance of the Ni-P-PTFE coatings were decreased drastically as the cerium concentration in the plating baths was exceeds 50ppm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.