Abstract
The effect of comonomer on structure and relaxation of flow-induced precursors was investigated in a series of isotactic polypropylene and random propylene–ethylene copolymers. The polymers were subjected to flow by fiber pulling and allowed to relax above their nominal melting temperature for specific times. The type of morphology developed after cooling revealed whether flow-induced precursors were still present or the melt had fully re-equilibrated. Precursors were long-lived and, at fixed temperature, decayed significantly faster with higher ethylene content. The critical time for precursor relaxation followed an Arrhenius-type dependence with temperature. The apparent energy of activation for precursor dissolution decreased with increasing comonomer content, indicating that the rate-limiting step of the relaxation process becomes less difficult with higher ethylene fraction. This effect is attributed to ethylene counits acting as disruptors of precursor structure and is discussed in terms of quasi-cr...
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.