Effect of prior cold work on tensile properties of Al–6Mg alloy with minor scandium additions

Abstract

Effect of aging on the mechanical properties of cold worked Al–6Mg alloy with minor additions of scandium is studied. Cast and mechanically worked samples are isochronally aged for 60 min at different temperatures up to 500°C. Evaluation of mechanical properties of the aged alloys is done at various strain rates of testing. The m-values (strain rate sensitivity) of the experimental alloys are desired from the tensile test results. The influence of scandium is much pronounced on yield strength than on the tensile strength. Alloys with higher scandium content have shown higher yield strength. The ‘m’ values are found to be comparatively high at peak aged condition of alloy with higher scandium content. The fracture of the experimental alloys occurs through microvoid coalescence.On étudie l’effet du vieillissement sur les propriétés mécaniques de l’alliage écroui d’Al-6Mg avec additions mineures de scandium. On a vieilli à durée égale pendant 60 minutes à différentes températures, jusqu’à 500°C, des échantillons moulés et formés mécaniquement. On fait l’évaluation des propriétés mécaniques des alliages vieillis par essai à différentes vitesses de déformation. On désire les valeurs de m (sensibilité à la vitesse de déformation) des alliages expérimentaux à partir des résultats de l’essai de traction. L’influence du scandium est beaucoup plus prononcée sur la limite d’élasticité que sur la résistance à la traction. Les alliages ayant une teneur plus élevée en scandium ont montré une limite d’élasticité plus élevée. On a trouvé que les valeurs de ″m″ étaient comparativement élevées sous la condition maximale de vieillissement de l’alliage ayant la teneur la plus élevée en scandium. La rupture des alliages expérimentaux se produisait par cupulation.