Abstract
The precipitate behavior during forging and ageing process of Mg–10Gd–2Y–0.5Zn–0.3Zr alloy has been investigated by X-ray diffraction, scanning electron microscopy and transmission electron microscopy. The mechanical properties of the alloy after forging and ageing process have been evaluated using Vickers hardness and room-temperature tensile tests. The results show that precipitation of 14H-type long period stacking order (LPSO) phase is the main strengthening phase in the as-forged alloy. The LPSO phase and refinement of grains contribute to the strength improvement of the alloy after forging process. The optimal mechanical properties of the alloy are obtained when it is aged at 200 °C for 60 h, which mainly owes to the precipitation of large amounts of β′ and 14H-type LPSO phases on the α-Mg matrix. The growth of secondary phases, widening of soft precipitate free zones and coarsening of grains during subsequent ageing process at higher temperature lead to the decrease of mechanical properties of the alloy.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call