Abstract
Objective A previous study found that the shear bond strength (SBS) to bovine enamel for the self-etching adhesive Adper Prompt-L-Pop (PLP) was 75% of that found with the etch-and-rinse material SingleBond, while the comparative value for the shear fatigue limit (SFL) was only 58% at 10 5 load cycles. Resin penetration into the enamel surface was substantially less for PLP but it was not conclusive that this was the reason for the lower results cited above. The objective of this study was to determine if pre-etching enamel would substantially improve the SBS and SFL of the PLP adhesive over those found in the previous study. Materials and methods All test methods were the same as for the previous study. SBS measurements were conducted for composite bonds to bovine enamel using a phosphoric acid pre-etch with the PLP adhesive (PLP-10) and for a conventional enamel-bonding adhesive (EB). Fatigue testing was done with the same test fixtures, load cycling at 2 Hz up to a maximum of 10 5 cycles at four selected peak load values between 35 and 60% of the respective bond strengths. Fatigue limits were determined from the data obtained. SEM analysis of resin penetration of the enamel surface was carried out for each adhesive. Results A significantly greater SBS and SFL were found for EB (SBS: 30.4 MPa; SFL: 15.6 MPa) than for PLP-10 (SBS: 20.2 MPa; SFL: 9.9 MPa). Compared with previously found results, the pre-etching of enamel had no significant improvement in SBS and only slight improvement in SFL. Resin tag penetration of the enamel surface for PLP-10 was similar to that previously found for PLP alone, suggesting that the porosity created by phosphoric acid was effectively removed by the acidic PLP adhesive. Significance Unlike some self-etching adhesives reported in the literature, pre-etching enamel did not improve the performance of the Prompt-L-Pop adhesive.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.