Abstract
Polycaprolactone with five different molecular weights was spin-coated on silicon wafers and plasma immersion ion implanted (PIII) with ion fluence in the range 5 × 1014-2 × 1016 ions/cm2. The effects of PIII treatment on the optical properties, chemical structure, crystallinity, morphology, gel fraction formation and wettability were investigated. As in the case of a number of previously studied polymers, oxidation and hydrophobic recovery of the PIII treated PCL follow second order kinetics. CAPA 6250, which has the lowest molecular weight and the highest degree of crystallinity of the untreated PCL films studied, has the highest carbonization of the modified layer after PIII treatment. Untreated medical grade PCL films, mPCL PC12 (Perstorp) and mPCL OsteoporeTM have similar chemical structures and crystallinity. Accordingly, the chemical and structural transformations caused by PIII treatment and post-treatment oxidation are almost identical for these two polymers. In general, PIII treatment destroys the nano-scale lamellar structure and results in a reduction of PCL crystallinity. Examination after washing PIII treated PCL films in toluene confirmed our hypothesis that cross-linking due to PIII treatment is significantly higher in semi-crystalline PCL as compared with amorphous polymers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Materials Science: Materials in Medicine
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.