Abstract
The planar anisotropy (PA) and tension-compression asymmetry (TCA) of the commercially pure titanium (CP-Ti) were investigated through uniaxial tension and compression experiments at room temperature. By deep drawing experiment, the formability and the earing profile for the CP-Ti were studied at room temperature. The deep drawing simulations using the hardening rules of uniaxial tensile or compression curves were compared with experimental results. The results show that the CP-Ti has obvious PA, and the plastic strain ratiosr0,r45andr90are 1.47, 1.64 and 2.05, respectively. The CP-Ti sheet shows the tension-compression asymmetry of yielding and hardening. The TCA also shows obvious PA. The tension-compression yield strength ratio of 0°, 45° and 90° to the rolling direction are 1.12, 1.08, 1.04, and the tension-compression hardening exponent ratio are 0.86, 0.8 and 0.62, respectively. The simulative results without considering TCA indicate that the forming force, the wall thickness and earing profile are not in good agreement with the experimental ones. Therefore, the earing appeared in 45° is contribution of the PA and TCA. The TCA will reduce the thickness of the deep drawing parts, increase the earing ratio and affect the drawing force.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.