Abstract

This study aims to investigate the effect of different particle sizes and pressures on the shear bond strength (SBS) and the roughness (Ra) of polyetheretherketone. A total of 117 polyetheretherketone specimens were fabricated and divided into a control (CN: no air-particle abrasion) and eight pre-treatment groups (air-abraded with 50- or 110-μm Al2O3 particles at 1(A), 1.5(B), 2(C), and 2.5(D) bar). The adhesive, Visio.link was used. Thermal aging was performed. Surface properties, SBS and failure mode were assessed. Data was analyzed by linear regression, Pearson correlation and Dunnett's T3 test for pairwise comparisons (p⟨0.05). The highest and lowest Ra were found in the 110D and CN groups respectively, and the highest SBS results were obtained from the 50B group. Pressure and particle size showed significant difference on the investigated properties (p⟨0.001). Only adhesive failure was observed in the CN, and resin cohesive failure was observed in addition to adhesive failure in the overall study groups. The air-borne particle abrasion procedures and the adhesive material combination are critical to the strength of the polyetheretherketone bond. The combination of visio.link with the pre-treatment option of 50-μm Al₂O₃ particles applied at 1.5-bar pressure delivered the most favorable results.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call