Abstract

Micron‐sized powders of neat aluminum and aluminum combined with 5 wt% gallium are prepared as flakes and spherical composites by emulsion‐assisted milling. Such powders are of interest as high‐energy‐density fuel additives to solid propellants, explosives, and pyrotechnics. Added gallium does not affect the size or shape of the prepared composites; it also does not change appreciably the oxidation kinetics of the prepared powders. All milled powders ignite readily when coated on an electrically heated filament, unlike the starting aluminum powder. Powders with added gallium ignite at slightly lower temperatures when heated rapidly. The liquid metal embrittlement effect due to added gallium might have caused a smaller microstrain in the refined, milled powders. However, it does not affect the oxidation. Instead, it is proposed that added gallium alters the natural amorphous alumina film, affecting its transition to a crystalline γ‐phase during rapid heating, and thus affecting the powder ignition.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.