Abstract
The effect of Nb addition (0.022, 0.053, 0.078wt%) on the hydrogen-induced delayed fracture resistance of 22MnB5 was studied by constant load test and electrochemical hydrogen permeation method. It is shown that the appropriate addition of Nb is beneficial to the improvement of the delayed fracture resistance of tested steel, especially when the steel contains high concentration of hydrogen, and the maximum delayed fracture resistance is obtained at a Nb content of 0.053%.The result of hydrogen permeation test shows that the diffusion coefficient of hydrogen in the steel containing niobium is lower than that in steel without niobium, which indicates that it is harder for hydrogen in the steels containing niobium to diffuse and aggregate. In addition, the reason for Nb improving the delayed fracture resistance of steels is discussed from two aspects: hydrogen trap effect and grain refinement effect. The analysis shows that the main reason leading to the improvement of the delayed fracture resistance is the hydrogen trapping effect of NbC while the grain refinement effect of Nb(C,N) secondary.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.