Abstract

This paper aims to achieve multi-scale crack control of concrete by using graphene oxide (GO) and macroscopic steel fiber in combination, and to reveal the multi-scale collaborative reinforcement mechanism of GO and steel fiber. A three-point bending fracture mechanics test was employed to analyze the macroscopic fracture properties of ultra-high performance concrete (UHPC) reinforced by GO, and a single fiber pull-out test was utilized to assess the impact of GO on the fiber–matrix interface properties. The results showed that 0.04% GO reinforced UHPC had the best fracture property, and steel fiber and GO showed good synergistic crack control effect. GO directly acted on controlling the cracking of concrete matrix at the nanoscale, thus improving the fracture energy of UHPC matrix by 14% from 73.08 N/mm to 83.39 N/mm. This micro-scale matrix reinforcement provided by GO further improved the pull-out property of steel fibers, and the pull-out energy dissipation of straight steel fibers and hook-end fibers was increased by 43.7% and 31.5%. A micromechanical prediction model for fracture energy of straight steel fiber UHPC was established, which could construct the quantitative relationship between UHPC fracture energy and micromechanical parameters. The model showed that the initial fiber–matrix bond strength (τ0) and slip hardening coefficient (k0) had a powerful influence on the UHPC fracture energy.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.