Effect of MnO content on the interfacial property of mold flux and steel

Abstract

The interfacial property between liquid mold flux and steel has significant impact on the quality of casting slab, and this property is mainly determined by the chemical composition of mold flux and the reaction between the flux and steel. The effect of MnO content on the contact angle and interfacial tension between liquid mold flux and ultra-low carbon steel was investigated by sessile drop method in this article, and the results suggested that both the contact angle and interfacial tension decreased with the increase of MnO content in the mold flux. The increase of Si and Mn and the reduction of Al and Ti in the interaction layer were caused by the chemical reactions occurred in the vicinity of interface between mold flux and steel substrate. Besides, the thickness of the interaction layer increased from 4 μm to 7 μm, then to 9 μm, 11 μm and 15 μm when the MnO content was added from 1 wt% to 3 wt%, then to 5 wt%, 7 wt%, and 9 wt% due to the fact that MnO can simplify the polymerized structure of the melt and improve the penetrability of molten mold flux to make the interfacial reaction easier.