Abstract
Deformation behavior of Nb–Si–Zr alloys is investigated at various temperatures ranging from R.T. to 1670 K. The master alloy ingots composed of Nb–18.1 at% Si–1.5 at% Zr doped with Mg are Ar-arc-melted. The ingots contain Nb rods (radius: 1 μm) in Nb 3Si matrix formed by eutectic reaction. Alloys are subjected to heat treatments at 1923 K for 4–100 h to obtain a large Nb network structure with small silicide (α-Nb 5Si 3) particles by decomposing Nb 3Si matrix into Nb and Nb 5Si 3 through a eutectoid reaction. Compression tests are conducted at room temperature in air and at elevated temperatures in Ar atmosphere. At 1471 K the maximum strength is 500 MPa and compressive ductility is higher than 10% with a strain rate of 1.0 × 10 −4 s −1, while at room temperature the maximum strength is over 1500 MPa and compressive ductility is about 1.5%. The high-temperature deformation obeys a power-law type equation. The stress exponent n is evaluated to be 4.8 and the apparent activation energy is 350 kJ/mol. The Vickers indentation at room temperature revealed that the crack propagation at room temperature is suppressed effectively by ductile Nb. This suggests that the Nb aggregate in the network structure acts as a large Nb grain containing fine Nb 5Si 3 particles, which might be beneficial for ductility at low temperatures.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.