Abstract
In this paper, the effect of laser parameters on fatigue life was investigated by laser irradiation for the undamaged and pre-damaged copper film specimens with thickness of 25μm. The results showed that the laser parameters have a great impact on the strengthening of original specimens and the healing of specimens with fatigue damage, and total fatigue life of the healed specimen with fatigue damage was longer than that of the strengthened original specimen. According to the obtained fatigue life results under different laser irradiation conditions, the optimal laser parameters were identified. The fracture morphology was observed by SEM. The results showed that, under the optimal laser parameters condition, a dense layer was found on the surface of specimen and the columnar grains were refined, which results in increasing the total fatigue life of the specimen.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.