Abstract
The effect of cold rolling on the microstructure evolution and mechanical properties of a cold rolled Fe-0.3C-17Mn-1.5AI TWIP steel was studied. The plate samples were cold rolled with reductions of 20, 40, 60 and 80%. The structural changes were associated with the development of deformation twinning and shear bands. The average spacing between twin boundaries in the transverse section of the rolled plates decreased from ~190 to 36 nm with an increase in the rolling reduction from 20 to 40%. Upon further rolling to 80% reduction the twin spacing remained at about 30 nm. The cold rolling resulted in significant increase in strength as revealed by tensile tests at an ambient temperature. The offset yield stress approached 1440 MPa, and the ultimate tensile strength increased to 1630 MPa after rolling reduction of 80%. Such significant strengthening was attributed to the development of specific structure consisting of deformation nanotwins with high dislocation density.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.