Effect of lamination layer thickness and abutment preparation on the fit of Co-Cr multi-unit prostheses fabricated by additive manufacturing: An in vitro study

Abstract

Statement of problemSelective laser melting has been increasingly used in the fabrication of metal-ceramic prostheses. The lamination layer thickness may influence the fit of the restoration. However, data regarding its impact remain scarce. PurposeThe purpose of this in vitro study was to evaluate the marginal and internal fit of cobalt-chromium (Co-Cr) 3-unit frameworks fabricated by additive manufacturing with different melting layer thicknesses on different abutments. Material and methodsThe first right maxillary premolar and molar from a typodont were prepared with a circumferential 1.2-mm chamfer, 2-mm occlusal reduction, and total taper of 8 degrees to receive 3-unit fixed partial dentures. After framework design, the data were sent to a laser machine, and 30 specimens were fabricated from Co-Cr metal powder (Mediloy S-Co) by selective laser melting. Specimens were assigned to 3 groups (n=10) with different lamination layer thicknesses of 25 (L25), 50 (L50), and 100 (L100) μm. Marginal fit and internal fit were evaluated. Results were compared among layer thickness groups and abutments. Data were compared by using the Levene test, t test, and ANOVA (α=.05). ResultsA statistical difference was found between different layer thickness groups (P=.016), but not between abutments (P=.429). On the abutment level, significant difference was found in the gap values for the molars (P=.049) between layer thickness groups, but not for the premolars (P=.126). Group L25 reported the smallest mean discrepancy values, and group L100 reported the highest, with statistical difference found between group L100 and groups L25 (P<.001) and L50 (P<.025), but not between groups L25 and L50 (P=.094). ConclusionsThe lamination layer thickness affected the adaptation of the metal frameworks. Framework fit did not significantly differ between abutments.