Abstract
La/Pb co-doped BiFeO3 compounds were prepared by a solid-state reaction. X-ray diffraction of BiFeO3 (BFO), Bi0.725La0.1Pb0.175FeO3 [BLPFO] showed single phase in nature. BFO crystallize in the rhombohedral distorted perovskite structure (space group-R3c) while to that BLPFO crystallize in distorted pseudocubic (Pm-3m) symmetry which has been confirmed by the Rietveld refinement of the room temperature X-ray powder diffraction data. The effect of La/Pb substitution on dielectric constant, and loss tangent, of the samples was studied at room temperature in a wide range of frequency 10 Hz – 1 MHz. The room temperature dielectric constant of BFO (BLPFO) was 120 (200). Ferroelectric measurement reveals remnants polarization of BLPFO is about 0.24 μC/cm 2 at an applied field of 15 kV/cm. Weak ferroelectric effect is observed for co-doped BiFeO3 compound.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.