Abstract
ABSTRACTSingle crystals of E21 (L12) Ni3AlC1-x were prepared by the unidirectional solidification using the optical floating zone melting method to determine their mechanical properties. Particularly the effects of interstitial carbon atoms on mechanical properties were evaluated by compression tests at room temperature. Operative slip system of E21 Ni3AlC is {111}<011> type which is the same as that of L12 Ni3Al. Strength of Ni3AlC single crystals increases with carbon concentration due to the solid solution effect, though the stress relief of yielding behavior is enhanced at the intermediate carbon content at around 3at%. A large gap appears in the carbon concentration dependence of critical resolved shear stress (as well as yield stress) at almost the same carbon content. This discontinuity in strengthening is attributed to the interaction between multiple solute carbon atoms and mobile dislocations.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.