Abstract
In this current investigation, SiC particles 20μm in average size were incorporated into the commercially AA6061-T6 to prepare surface composite by using Friction stir processing (FSP). The morphology of the reinforcement inside the Al matrix has been evaluated from scanning electron microscope (SEM) and the corrosion characteristics of the resulted composite were evaluated using static immersion corrosion (SIC) behavior in 3.5% NaCl aqueous solution at various regimes. From the results, it observed that the SiC particles were distributed uniformly inside the stir zone (SZ) in both first and third-pass of FSP. The micro hardness of stir zone with SiC particles of I-pass was higher compared to III-pass and as-received Al alloy. In static immersion corrosion test the FSP AA6061-T6/SiCp exhibited significantly greater corrosion resistance in I-pass than compared to the III-pass and as-received Al alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: International Journal of Applied Research in Mechanical Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.