Effect of hydrogen on Ca and Mg acceptors in GaN

Abstract

The influence of minority carrier injection on the reactivation of hydrogen passivated Mg in GaN at 175 C has been investigated in p-n junction diodes. The dissociation of the neutral MgH complexes is greatly enhanced in the presence of minority carrier and the reactivation process follows second order kinetics. Conventional annealing under zero-bias conditions does not produce Mg-H dissociation until temperatures {ge} 450 C. These results provide an explanation for the e-beam induced reactivation of Mg acceptors in hydrogenated GaN. Exposure to a hydrogen plasma at 250 C of p-type GaN (Ca) prepared by either Ca{sup +} or Ca{sup +} plus P{sup +} coimplantation leads to a reduction in sheet carrier density of approximately an order of magnitude (1.6 {times} 10{sup 12} cm{sup {minus}2} to 1.8 {times} 10{sup 11} cm{sup {minus}2}), and an accompanying increase in hole mobility (6 cm{sup 2}/Vs to 18 cm{sup 2}/Vs). The passivation process can be reversed by post-hydrogenation annealing at 400--500 C under a N{sub 2} ambient. This reactivation of the acceptors is characteristic of the formation of neutral (Ca-H) complexes in the GaN. The thermal stability of the passivation is similar to that of Mg-H complexes in material prepared in the same manner (implantation)more » with similar initial doping levels. Hydrogen passivation of acceptor dopants in GaN appears to be a ubiquitous phenomenon, as it is in other p-type semiconductors.« less