Abstract
The impact of femoral head surface roughness on wear of gamma-irradiation sterilized (3 MRad in nitrogen, crosslinked) and nonsterilized (not crosslinked) UHMWPE acetabular cups has been evaluated. Gravimetric wear testing was performed in a hip joint simulator for 2 x 10(6) cycles. CoCrMo heads were used with different surface roughness (R(a) = 15 nm and R(a) = 400 nm). The surface roughness after wear test was unchanged for the roughened heads, whereas the initially smooth heads showed a few scratches. The roughened heads increased the wear of the acetabular cups 2-fold. The gamma-irradiated cups tested against rough heads underwent the highest wear. The absorption of water was highest for the gamma-irradiated cups (0.0204% compared to 0.0031% after 85 days). Raman spectroscopy showed small but significant crystallinity changes in the wear zone, where the gamma-irradiated cups with the most extensive abrasion increased in crystallinity, whereas the nonsterilized cups underwent a crystallinity decrease.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.