Abstract
Nowadays, application of cermet coatings deposited by High-Velocity Oxygen-Fuel (HVOF) has received considerable attention in a variety of industries. Carbide coatings have high surface roughness, so it is essential to grind the coated surface. The present investigation studied the effect of simultaneous changes in the grinding parameters including the depth of cut, feed rate and cutting speed on the fracture toughness of the WC-10Co-4Cr coating sprayed by HVOF. The fracture toughness was measured using the Vickers Indentation Test on the cross-sectional surface of the coating. A full factorial design of experiment was selected for experimental planning and the analysis of variance was employed to find the effect value of grinding parameters on output. The results revealed that the fracture toughness of the WC-10Co-4Cr coating increases after grinding due to the higher compressive residual stresses. The fracture toughness of coating increases with the decrease of the cutting speed and the increase of the depth of cut and feed rate. The most effective grinding parameters are depth of cut, feed rate and cutting speed, respectively. At the end of the current study, a mathematical model between grinding parameters and the fracture toughness of the coating was proposed using the regression analysis.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.