Abstract
Thermal diffusivity of AlN‐based ceramics was studied as a function of second‐phase amount and heat‐treatment time. The Y2O3·Al2O3 contents varied over the range of 13‐31 vol%. The thermal diffusivity decreased as the amount of second phase increased. After sintering at 1850°C, the AlN ceramics consisted of rounded, largely isolated grains. Heat treatment of these samples for 5‐50 h at 1800°C resulted in microstructures that consisted of largely contiguous AlN grains. There was a substantial increase in the thermal diffusivity after the heat‐treatment step, and the incremental improvement was essentially constant for the three compositions that have been studied. The amount of second phase was unchanged during heat treatment; therefore, the increase in thermal diffusivity is assumed to be a direct result of the enhanced contiguity of AlN grains.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.