Abstract
Lightweight metallic alloys in the transport sector are the essential choice to reduce carbon monoxide emissions. Magnesium (Mg) can serve this purpose appreciably because it has a low density compared to other metallic metals and a high strength in a small portion of metals. The reason behind this is having very low weight. Notwithstanding the alloys exhibit high susceptibility to corrosion especially galvanic corrosion, which impedes it from its various applications. The corrosion resistance of magnesium alloy depends largely on the surface film whether it can protect well and the corrosion due to galvanic effect between the second phase particles or microstructures and the magnesium matrix. Role of second phase particles eventually improves the corrosion property by enhancing its resistance to corrosion. Mg-4Zn being a promising alloy, 3 wt% Gd has been added further to investigate the corrosion resistant properties of Mg-4Zn-3Gd alloy. After preparing the alloys by casting method in induction furnace followed by homogenization at 410°C, the sample was hot rolled at 400°C. Preparation of the samples has been verified by EDS, XRF and XRD analysis. Corrosion study has been done for 1 hour, 24 hours and 72 hours. Microstructures have been taken for as cast, homogenized, and as rolled condition before corrosion test. The analysis shows a large difference in the grain size and phase distribution. Due to dynamic recrystallization during rolling hardness also shows differences compared to as cast and homogenized sample. The corrosion test is performed by weight loss test, electrochemical measurement, and immersion test. In the results, it has been seen an increase in corrosion rate at the initial stage, however it came to a constant rate after some time. After corrosion test, optical micrographs (OM) and scanning electron microstructures (SEM) images show typical morphology of corroded surface with some micro cracks. The presence of Gd in Mg-4Zn alloy enhanced the corrosion performance when it is done for longer time.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.