Abstract
Fe–MnO2–Fe2O3–sucrose–epoxy resin and self-reactive quenching technology were used to prepare two kinds of hollow multiphase ceramic microspheres (HMCMs). The results obtained by high-speed photography, SEM, XRD and laser particle size analysis showed that the flame field partition (“edge region”, “junction region” and “center region”) and different flight combustion behaviors of particles (“self-burst”, “collision effect” and “self-diminution”) are the main reasons to generate different intrinsic characteristics (particle size, microstructure and chemical composition) between coarse and fine HMCMs. On the one hand, these differences resulted in different electromagnetic parameters. Coarse HMCMs, owing to low resistivity, Fe–Fe3+ dipoles formed and more defects or vacancy, possessed higher dielectric loss. And due to the same main phase (MnFe2O4), the two kinds of HMCMs have close magnetic properties, however, the magnetic loss of fine HMCMs will move to low-frequency which resulted from infinite solid solution formed. On the other hand, different optimal match thickness (dcoarse=2.5mm and dfine=2mm), minimum reflectivity (Rcoarse=−24dB and Rfine=−25dB) and effective absorption bandwidth (fcoarse=4GHz and ffine=4.2GHz) were caused by these differences. This also illustrate that the match thickness will reduce along with the decrease of particle size. In addition, the two kinds of HMCMs belong to dielectric loss dominated material. And in the same thickness (2mm), because of low permittivity of fine HMCMs, the electromagnetic match property was improved to broaden effective absorption bandwidth (4GHz).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.