Effect of electropulsing rolling on mechanical properties and microstructure of AZ31 magnesium alloy

Abstract

Electropulsing rolling (ER) and warm rolling (WR) processes were performed to roll AZ31 magnesium alloy sheets. Mechanical properties, microstructure and texture evolution of these specimens were investigated after rolling. The results indicate that electropulsing accelerates the recrystallization of AZ31 alloy sheets during hot rolling. After electropulsing rolling at a relatively low temperature, the microstructure of the sample shows fine equiaxed recrystallized grains with a lower density of dislocations and precipitates. In contrast, the microstructure of the sample after warm rolling shows elongated grain, numerous deformed twins, and a high density of dislocation and precipitates. Electropulsing rolling helps weaken the basal fiber texture. Although both the alloy sheets (ER and WR) have typical basal fiber texture, the maximum pole intensity of basal in ER sample is weaker. ER sheet has higher yield strength and elongation compared to WR sheet. As a promising technique, electropulsing rolling can be used to improve the microstructure and mechanical properties of materials.