Abstract
The purpose of the present study was to evaluate the effect of dual-peak LED on the polymerization of coinitiator-containing composite resins. For this, microhardness, degree of conversion (DC), and polymerization shrinkage were evaluated. Specimens (coinitiator-containing: Aelite LS Posterior, Tetric EvoCeram, and Vit-l-escence; only camphorquinone-containng: Filtek Z350 and Grandio) were light cured using a quartz-tungsten-halogen (QTH: OP), a single-peak light-emitting diode (LED) (L. E. Demetron: DM), and a dual-peak LED (G-light: GL), respectively. All specimens light cured using GL showed the highest microhardness both on the top and bottom surfaces compared with the values obtained using the rest light-curing units (LCUs). DC had no consistent trend correspond to the LCU, but rather product specific. OP yielded the lowest polymerization shrinkage on the specimens. The coinitiator-containing composite resins achieved the highest microhardness by the dual-peak LED (GL). However, the influence of GL on DC and polymerization shrinkage of the specimens was not consistent.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.