Abstract
AbstractIn our research, the effect of D‐lactide content in injection‐molded and annealed poly(lactic acid) (PLA) was investigated for crystallinity as well as crystalline forms (less‐ordered α′ and more‐ordered α crystalline forms) and thus on the mechanical, heat deflection temperature (HDT), and creep properties. Three different PLA grades 3052D, 3001D, and 3100HP were investigated with D‐lactide contents of 4%, 1.4%, and 0.5%, respectively. The injection‐molded PLA specimens were then postproduction annealed in a heat chamber at 80–140 °C for 1 h to develop various crystallinities and various ratios of α′ and α crystal forms. It was demonstrated that not only annealing but also the D‐lactide content significantly influences the crystallization, crystal structure, and accordingly properties of PLA like notched Charpy impact strength, HDT, and creep characteristics. Higher HDT, impact properties, and creep resistance could be reached by using PLA with lower D‐lactide content with a certain annealing temperature range to develop definite crystal structures. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci. 2019, 136, 47103.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.