Abstract

The objectives of this study were to evaluate the micro-tensile bond strength (μTBS) of composite bonded to human occlusal sclerotic dentin following different surface treatments to determine the sclerotic dentin morphology. Human molars without (normal dentin; group 1) or with occlusal wear (sclerotic dentin; groups 2-5) were divided and subjected to different surface treatments, including the normal protocol for the Contax self-etch bonding system (group 1 and 2); doubled etch-prime time (group 3); pre-conditioning with 37% phosphoric acid before normal protocol (group 4); or pre-conditioning with 37% phosphoric acid before doubling the self-etching time (group 5). All teeth were restored with composite (Luxacore Z dual), sectioned into stick specimens and stored for 24h in water before specimens were subjected to the μTBS test (n=50 per group). The μTBS of normal dentin was not statistically significantly different from that of the sclerotic dentin groups, except for the doubled etch-prime time group which showed lower μTBS. Sclerotic dentin pre-treated with phosphoric acid resulted in less sclerotic casts and wider dentinal tubules, while doubled etch-prime time did not alter the morphology, as shown by scanning electron microscopy. In conclusion, the use of 37% phosphoric acid before applying self-etch bonding resulted in more tubule openings and a significantly higher μTBS when compared with the doubled etch-prime time group.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.