Abstract
To evaluate the effect of different surface treatments and adhesive cementation on the miniflexural strength (MFS) of monolithic zirconia. Two-hundred and forty (240) sintered bars of translucent zirconia (ZT) and ultra-translucent zirconia (ZUT) were obtained (8 mm ×2 mm ×1mm). The bars were divided into 16 groups (n = 15) according to the factors "Zirconia" (ZT and ZUT), "Cementation" (Cem) and "surface treatment" (Ctrl:Control, Al:Aluminum oxide/Al2O3 50 µm, Si:Silica/SiO2 coated alumina particles oxide 30 µm, Gl:Glazing+hydrofluoric acid). Half of the bars received an adhesive layer application, followed by application of resin cement and light curing. The surface roughness was measured in non-cemented groups. All the bars were subjected to the MFS test (1.0mm/min; 100 kgf). Scanning electron microscopy was used for qualitative analyses. MFS data (MPa) and roughness (µm) were statistically evaluated by three-way and two-way ANOVA respectively and Tukey's test (5%). The surface treatment and the interaction were significant for roughness. Glazing promoted less roughness compared to silicatization. Regarding MFS, only the zirconia and surface treatment factors were significant. For ZT, the sandblasted groups had an increase in MFS and glazing reduced it. There was no difference between the groups without cementation for the ZUT; however, ZUT.Si/Cem, and ZUT.Al/Cem obtained superior MFS among the cemented groups. Sandblasting increases the flexural strength for ZT, while glaze application tends to reduce it. Applying resin cement increases the flexural strength of ZUT when associated with sandblasting. Sandblasting protocols promote greater surface roughness.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Similar Papers
More From: Journal of prosthodontics : official journal of the American College of Prosthodontists
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.