Abstract
Crack healing has great effect on monotonic strength of ceramics. Also the crack-healing effect on fatigue behavior is an interesting issue. Three kinds of Al2O3/30 vol.% SiC composites that have differences in crack-healing ability and fracture toughness were hot pressed. Static fatigue behaviors of these crack-healed specimens were investigated. From the experimental results, the static fatigue limits of three kinds of Al 2O3/30 vol.% SiC composites were 800, 700, and 1000 MPa, respectively. Furthermore, the fractures seldom initiated from the healed crack. Therefore, it was found that using the crack-healing forbade stress corrosion cracking from the original surface cracks, thereby leading to large increment in fatigue strength. The results, however, demonstrated that fatigue cracks were generated by applying high tensile stress. The general mechanism of fatigue cracks was discussed by using surface morphology.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Intelligent Material Systems and Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.