Abstract
Multicomponent TiAlCrN and TiAlCrCN coatings were deposited using vacuum arc evaporation technique on AISI 430 stainless steel. The influence of working gas pressure, C/N ratio, bias voltage on the structure and tribomechanical properties of the obtained coatings has been studied. The surface morphology, chemical compound of the coatings obtained under the various conditions has been analyzed by SEM with EDX, XRD, and XRF analysis. The dry wear pad-on-disc tests against 100Cr6 counterbody at 20 N load have been carried out. It was established that Vickers micro-hardness was varied from 26 to 41 GPa depending on deposition parameters.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.