Abstract
Abstract Lead-free Bi0.5(Na0.80K0.20)0.5TiO3 (BNKT) ferroelectric films were synthesized on Pt/Ti/SiO2/Si substrates via the chemical solution deposition. The influence of the crystallization temperature on the microstructures, the ferroelectric and energy-storage properties of the films was investigated in detail. The results showed that the BNKT films have reached the well crystallized state in the single-phase perovskite structure at 700 °C. Ferroelectric and energy-storage properties of the films were significantly enhanced by increasing the crystallization temperature. The remnant polarization (2Pr) and maximum polarization (2Pm) reached the highest values of 18.4 μC/cm2 and 61.2 μC/cm2, respectively, under an applied electric field of 300 kV/cm. Thanks to the strong enhancement in 2Pm and the large Pmax - Pr value, the highest energy-storage density (Jreco) and efficiency of 2.3 J/cm3 and 58.2%, respectively, were obtained. These results indicate that the BNKT films have application potentials in advanced capacitors.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Science: Advanced Materials and Devices
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.