Abstract
The impact of the crystallinity on structural, thermal, and in vitro dissolution properties were examined for Na2O-CaO-Nb2O5/MgO-P2O5 glasses/glass-ceramics. Glass-ceramics were synthesized via a spontaneous crystallization process. The Nb content in the materials increased with melting temperature, furthermore, the crystallinity is proportional to the Nb content. The presence of crystalline niobates and phosphates is confirmed by FTIR analysis which is consistent with XRD. The FTIR results indicate that the phosphate network is built of different proportions of Q2, Q1, and Q0 units, depending on the amount and type of crystalline phase. Most of the samples show an improvement in thermal stability. The in vitro dissolution test showed that the highest mass loss for most of the samples occurred during the first 6 days of immersion in the PBS solution. The presence of small phosphate crystals favors the deposition of hydroxyapatite on samples’ surfaces while the larger niobate crystals dissolve more readily.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.