Abstract
Young’s modulus of tapered mixed composition (zinc-blende with a high density of twins and wurtzite with a high density of stacking faults) gallium phosphide (GaP) nanowires (NWs) was investigated by atomic force microscopy. Experimental measurements were performed by obtaining bending profiles of as-grown inclined GaP NWs deformed by applying a constant force to a series of NW surface locations at various distances from the NW/substrate interface. Numerical modeling of experimental data on bending profiles was done by applying Euler–Bernoulli beam theory. Measurements of the nano-local stiffness at different distances from the NW/substrate interface revealed NWs with a non-ideal mechanical fixation at the NW/substrate interface. Analysis of the NWs with ideally fixed base resulted in experimentally measured Young’s modulus of 155 ± 20 GPa for ZB NWs, and 157 ± 20 GPa for WZ NWs, respectively, which are in consistence with a theoretically predicted bulk value of 167 GPa. Thus, impacts of the crystal structure (WZ/ZB) and crystal defects on Young’s modulus of GaP NWs were found to be negligible.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.