Abstract
M-type hexagonal ferrite, SrFe12-2xCrxBixO19 (x = 0.0–0.2) was prepared using sol-gel auto combustion technique. X-ray diffraction (XRD), Fourier transform infra-red (FTIR), Raman spectroscopy, field emission scanning electron microscopy (FESEM), UV–Vis–NIR spectroscopy, vibrating sample magnetometer (VSM) and impedance analyzer were respectively used to investigate the structural, optical, electrical and magnetic properties of the synthesized materials. XRD analysis reveals the formation of single phase of M-type hexaferrite with crystallite size ranging from 33 to 42 nm. The presence of peaks at 441, 552, and 598 cm−1 in the FTIR spectra indicate the formation of hexaferrite phase. FESEM images shows agglomerated particles having almost hexagonal shapes. The band gap of the material lies between 1.71 and 1.96 eV. The saturation magnetization and remanence enhances with increasing Cr3+-Bi3+ concentration. The dielectric constant and dielectric loss tangent decrease with increase in frequency while AC conductivity shows an increase at higher frequencies.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.