Abstract
AbstractThe study investigates the practical application of cyclic wet/dry corrosion tests in simulated industrial atmospheres to assess the impact of chromium (Cr) on the protective properties of vanadium micro‐alloyed weathering steels. Two types of steels were examined: a V‐N steel and a V‐N‐Cr micro‐alloyed weathering steel. These steels were subjected to corrosion tests with 0.01 mol/L NaHSO3 at a pH range of 4.4–4.8 for varying durations. The findings indicate that the inclusion of Cr in the composition of vanadium micro‐alloyed weathering steel enhances corrosion resistance and leads to the accumulation of Cr in the inner rust layer. Furthermore, the distribution of corrosion‐resistant elements (Cr, Ni, Cu, P, and Mo) in V‐N and V‐N‐Cr steels is analyzed. The rust layer was observed to exhibit stratification in the corrosive environment, with the outer layers being dense and uniform, while the inner layers were porous and exhibited poor adhesion to the matrix. The study also delves into the anticorrosion mechanism of vanadium weathering steel using techniques such as X‐ray diffractometer, electron probe microanalysis, and potential‐phase diagram.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.