Abstract
In the present work, the effect of artificial ageing of AA2024-T3 on the tensile mechanical properties and fracture toughness degradation due to corrosion exposure will be investigated. Tensile and fracture toughness specimens were artificially aged to tempers that correspond to Under-Ageing (UA), Peak-Ageing (PA) and Over-Ageing (OA) conditions and then were subsequently exposed to exfoliation corrosion environment. The corrosion exposure time was selected to be the least possible according to the experimental work of Alexopoulos et al. (2016) so as to avoid the formation of large surface pits, trying to simulate the hydrogen embrittlement degradation only. The mechanical test results show that minimum corrosion-induced decrease in elongation at fracture was achieved for the peak-ageing condition, while maximum was noticed at the under-ageing and over-ageing conditions. Yield stress decrease due to corrosion is less sensitive to tempering; fracture toughness decrease was sensitive to ageing heat treatment thus proving that the S΄ particles play a significant role on the corrosion-induced degradation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.