Abstract
The effect of cooling on the mechanical properties of hot-rolled high strength steels was investigated in order to improve the stretch-flangeability of conventional TS 590 MPa grade for the automotive parts through laboratory simulation and mill-scale production. The low temperature coiling method using a 3-step controlled cooling pattern after hot rolling was very effective for producing Nb-bearing high strength steel with high stretch- flangeability. It was suggested that the suppressed precipitation of grain boundary cementites and the decreased hardness difference between the ferrite matrix and bainite phases cause the excellent stretch-flangeability of ferrite-bainite duplex microstructure steel. Therefore, the formation and propagation of microcracks were suppressed relative to conventional HSLA steel with the ferrite and pearlite microstructure. In addition, the elongation improved compared with that of hot-rolled steel sheets using the conventional early cooling pattern because the volume fraction of polygonal ferrite increased.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.