Effect of Colloidal Silica as Abrasive on Low-k Dielectric Materials in Chemical Mechanical Planarization

Abstract

With low-k dielectric materials taking the place of oxide dielectrics as the primary dielectric materials, the low-k dielectric materials and interconnection Cu metals during Chemical Mechanical Planarization (CMP) is becoming a critical surface quality issue as well. In this study, experiments are carefully designed and conducted to investigate the effects of colloidal silica under compared acidic slurry and self-prepared alkaline slurry on k value of low-k dielectric materials, and in both of the slurry, colloidal silica (20~30nm) was used as polishing abrasive. The results showed that k value of low-k dielectric materials both increased within a similar range (self-prepared alkaline slurry, 3.27~3.33; commercial acidic slurry, 3.26~3.32), however, the results showed a obviously different result from reference’s report.