Abstract
Aqueous corrosion characteristics of iron aluminides in thiosulfate-chloride solution were studied as a function of chromium addition. Four kinds of iron aluminides, namely, FA-61, FA-77, FA-72 and FA-78, were prepared by arc melting followed by thermomechanical treatment. The corrosion behavior in thiosulfate-chloride solution for the prepared alloys were investigated by electrochemical tests (potentiodynamic test, potentiostatic test and electrochemical impedance spectroscopy (EIS) measurement) and surface analyses. The results of the potentiodynamic test indicated that the breakdown potential increased with increasing Cr content. Cr additions were found to prevent passive film from undergoing pitting corrosion. In EIS measurement, the depression angle was inversely related to pitting resistance, and decreased with increasing chromium content. The SEM observations of the sample surfaces reveal the different forms of pit as a function of chromium content. The AES results give evidence that the thiosulfate ions are reduced on the metallic surface, which inhibits the repassivation process.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.