Effect of Biaxial Isothermal Quasi-Continuous Deformation on Structure and Shape Memory Properties of Ti-Ni Alloys

Abstract

Severe plastic deformation (SPD) of Ti-50.0 at.% Ni alloy was carried out using the multi-axial deformation MaxStrain module of Gleeble system at 400, 370, 350 and 330 °C with accumulated true strains from e = 3.5 to 9.5. Kinetics of martensitic transformations was studied by DSC method, the structure features by x-ray diffraction and TEM. The recoverable strain was studied using a bending mode for strain inducing. A mixed nanocrystalline and nanosubgrained structure with average grain/subgrain size below 100 nm has been formed in a bulk sample as a result of SPD at as low as 330 °C. The resulting nanostructure provides an obvious advantage in the completely recoverable strain (9.3%) as compared to SPD at 350-400 °C (7-8%), and to reference treatment (2.5%). That correlates with Vickers hardness changes versus SPD strain.